| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | mtc-m16.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 6qtX3pFwXQZsFDuKxG/Cxhhs |
| Repositório | sid.inpe.br/marciana/2004/06.22.13.35 (acesso restrito) |
| Última Atualização | 2014:06.25.16.28.24 (UTC) marciana |
| Repositório de Metadados | sid.inpe.br/marciana/2004/06.22.13.35.22 |
| Última Atualização dos Metadados | 2021:03.04.02.28.22 (UTC) administrator |
| Chave Secundária | INPE-10741-PRE/6200 |
| ISBN/ISSN | 0925-9635 |
| ISSN | 0925-9635 |
| Chave de Citação | SilvaFraYokFerCor:2002:SyRaXr |
| Título | Synchrotron radiation X-ray analysis of boron-doped diamond films grown by hot-filament assisted chemical vapor deposition  |
| Projeto | DIMARE: Diamante e materiais relacionados |
| Ano | 2002 |
| Mês | Feb |
| Data de Acesso | 03 maio 2024 |
| Tipo de Trabalho | journal article |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 147 KiB |
| 2. Contextualização | |
| Autor | 1 Silva, Leide Lili Gonçalves da 2 Franco, Margareth K. 3 Yokaichiya, Fabiano 4 Ferreira, Neidenei Gomes 5 Corat, Evaldo José |
| Grupo | 1 LAP-INPE-MCT-BR 2 3 4 LAS-INPE-MCT-BR 5 LAS-INPE-MCT-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais, Laboratório Associado de Sensores e Materiais (INPE.LAS) 2 Laboratório Nacional de Luz Sincotron (LNLS) 3 Universidade Estadual de Campinas (UNICAMP) 4 Instituto Nacional de Pesquisas Espaciais (INPE) 5 Instituto Nacional de Pesquisas Espaciais (INPE) |
| Endereço de e-Mail do Autor | 1 leide@plasma.inpe.br 2 3 4 neidenei@las.inpe.br 5 corat@las.inpe.br |
| Revista | Diamond and Related Materials |
| Volume | 11 |
| Número | 2 |
| Páginas | 153-159 |
| Histórico (UTC) | 2006-09-28 22:25:43 :: administrator -> marciana :: 2008-02-18 17:38:09 :: marciana -> administrator :: 2014-06-25 16:23:20 :: administrator -> marciana :: 2002 2014-06-25 16:28:25 :: marciana -> administrator :: 2002 2021-03-04 02:28:22 :: administrator -> marciana :: 2002 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | materials physics boron-doped diamond synchrotron radiation X-ray diffraction diamante radiação difração de raio X |
| Resumo | This paper presents a synchrotron X-ray radiation analysis of boron-doped diamond films grown by hot-filament assisted chemical vapor deposition (HFCVD). The diamond films were grown at different doping levels with the introduction of boron to the gas mixture by bubbling hydrogen in a B2O3 solution in methanol. The B/C ratio in methanol varied from 2000 to 20 000 ppm and the gas flow rates were controlled so that boron incorporation to the film varied in the range from 10(18) to 10(21) boron/ cm(3). All other process parameters were kept unchanged to allow comparison only of the influence of the doping level. The film. analyses were performed at the X-ray diffraction beamline of the Laboratorio Nacional de Luz Sincrotron - LNLS, Brazil. The Debye-Scherrer configuration was used in this study. A high intensity monochromatic beam at lambda = 1.46 A was used and an excellent signal to noise ratio was obtained for 2theta varying from 20degrees to 150degrees. The difractogram for the undoped diamond film show intense peaks from the (111), (220), (311), (400) and (331) crystallographic planes. For the boron-doped films a set of new diffraction lines appear and their intensities increase considerably with the doping level. The set of diffraction peaks of similar intensities are related to a hexagonal structure and were assigned with hi-h confidence to tungsten carbide. This reveals that the boron-doping process in HFCVD facilitates the incorporation of tungsten carbide from the filament in the diamond film. The FWHM analysis of the diamond diffraction peaks shows a dependence of film crystallinity with doping level with a definite maximum at approximately 2.3 X 10(19) boron/cm(3). |
| Área | FISMAT |
| Arranjo 1 | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Synchrotron radiation X-ray... |
| Arranjo 2 | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Synchrotron radiation X-ray... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | 1-s2.0-S0925963501005738-main.pdf |
| Grupo de Usuários | administrator marciana |
| Grupo de Leitores | administrator marciana |
| Visibilidade | shown |
| Detentor da Cópia | SID/SCD |
| Política de Arquivamento | denypublisher denyfinaldraft24 |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 8JMKD3MGPCW/3ET2RFS |
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.25.21.49 3 |
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX. |
| Acervo Hospedeiro | sid.inpe.br/banon/2003/08.15.17.40 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyright creatorhistory descriptionlevel doi e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress resumeid rightsholder schedulinginformation secondarydate secondarymark session shorttitle sponsor subject tertiarymark tertiarytype url |
| 7. Controle da descrição | |
| e-Mail (login) | marciana |
| atualizar | |